低温等离子体改善义齿基托表面润湿性的研究

北京大学学报（自然科学版）

低温等离子体改善义齿基托表面润湿性的研究

潘红¹,王国敏²,孙志辉³,叶帼嫔¹,孙科¹,潘洁⁴,张珏^2,5,王静¹

1. 兰州大学口腔医学院, 兰州 730000; 2. 北京大学前沿交叉学科研究院, 北京 100871; 3. 北京大学口腔医院材料研究室, 北京 100081; 4. 北京大学口腔医院综合科, 北京100081; 5. 北京大学工学院, 北京 100871;

收稿日期:2013-03-05 出版日期:2014-03-20 发布日期:2014-03-20

Surface Wettability Improvement of Heat Curing Acrylic Resin by Non-thermal Atmospheric Pressure Plasma

PAN Hong¹, WANG Guomin², SUN Zhihui³, YE Guopin¹, SUN Ke¹, PAN Jie⁴,ZHANG Jue^2,5, WANG Jing¹

1. School of Stomatology, Lanzhou University, Lanzhou 730000; 2. Academy for Advanced Interdisciplinary Studies, Peking University, Beijing 100871; 3. Dental Materials Laboratory, School and Hospital of Stomatology, Peking University, Beijing 100081; 4. Department of General Dentistry, School and Hospital of Stomatology, Peking University, Beijing 100081; 5. College of Engineering, Peking University, Beijing 100871;

Received:2013-03-05 Online:2014-03-20 Published:2014-03-20

摘要/Abstract

摘要： 使用直流电激发4种工作气体(Ar, Ar/O₂, Ar/O₂/N₂和He/O₂)来产生等离子体, 分别处理热凝树脂样本1, 2, 4, 6, 8, 10分钟, 每组9个样本。使用接触角测量仪测量处理前后各样本的接触角; 利用发射光谱(OES)对等离子体的活性成分进行分析; 采用X射线光电子能谱(XPS)分析其表面的元素价键改变。经过Ar, Ar/O₂, Ar/O₂/N₂和He/O₂等离子体处理后, 热凝树脂表面的润湿性均显著增加, 处理 1 分钟时, 样本表面的接触角与原始值相比, 显著减小(p<0.001), 随着时间的延长, 减小趋势变缓。OES结果显示等离子体的活性成分中包含有大量的?OH; XPS分析表明: 经过等离子体处理后, 热凝树脂表面的C元素与O元素的比例减小, 有新的亲水性基团C?OH产生。大气压低温等离子体处理热凝树脂表面后, 产生新的亲水性基团C?OH, 从而增加表面亲水性。研究结果提示低温等离子体可能为临床上处理义齿基托树脂提供新方法。

关键词: 低温等离子体, 热凝丙烯酸树脂, 接触角, 润湿性, X射线光电子能谱, 发射光谱

Abstract: Plasma was generated by high voltage direct current, and four working gases were Ar, Ar/O₂, Ar/O₂/N₂ and He/O₂. The treatment time of each gas group was 1, 2, 4, 6, 8, 10 min, respectively. There were 9 samples in each group. Contact angle measurement instrument was employed to detect the contact angle before and after treatment; plasma components were analyzed by the optical emission spectroscopy (OES); elemental composition and chemical bond changes were measured by X-ray photoelectron spectroscopy analysis (XPS). After four plasma treatments, the surface wettability of the heat curing acrylic resin was significantly improved. After 1 min treatment, the water contact angle was significantly reduced (p<0.001), and presented clear slowdown trend over time. There existed plenty of ?OH in the plasma components according to the OES result. XPS analysis result indicated reduction of C and O proportion, and a new hydrophilic group C?OH was generated. After plasma treatments, the new hydrophilic group C?OH was formed on the surface of the heat curing acrylic resin, and this is a reasonable explanation of why the surface wettability was significantly improved after plasma treatment. It is suggested that non-thermal atmospheric pressure plasma may possess a good perspective in clinical use of denture base resin.

Key words: non-thermal atmospheric pressure plasma, heat curing acrylic resin, contact angle, wettability, X-ray photoelectron spectroscopy analysis (XPS), optical emission spectroscopy (OES)

中图分类号:

R783

潘红,王国敏,孙志辉,叶帼嫔,孙科,潘洁,张珏,王静. 低温等离子体改善义齿基托表面润湿性的研究[J]. 北京大学学报（自然科学版）.

PAN Hong,WANG Guomin,SUN Zhihui,YE Guopin,SUN Ke,PAN Jie,ZHANG Jue,WANG Jing. Surface Wettability Improvement of Heat Curing Acrylic Resin by Non-thermal Atmospheric Pressure Plasma[J]. Acta Scientiarum Naturalium Universitatis Pekinensis.

导出引用管理器 EndNote|Ris|BibTeX

链接本文: https://xbna.pku.edu.cn/CN/

https://xbna.pku.edu.cn/CN/Y2014/V50/I2/235

[1]	彭科, 刘玥汐, 陈良, 卢新培. 磁场固定串联辉光等离子体固氮特性研究[J]. 北京大学学报自然科学版, 2023, 59(6): 915-922.
[2]	母云涛;郑殿峰;王玉清;李立翰;张会强. 丙烷/空气低温等离子体点火起爆数值研究[J]. 北京大学学报（自然科学版）, 2015, 51(5): 791-798.
[3]	国晋菘,潘洁,张茜,吴杉,梁永栋,王静. 大气压低温等离子体的活性氧成分分析及其杀菌效应研究[J]. 北京大学学报（自然科学版）, 2012, 48(4): 533-537.